D266
Description:
D266 is low hydrogen potassium type coating high manganese steel surfacing electrode can be AC ??and DC (AC welding, no-load voltage of not less than 70V), surfacing should adopt a small current, narrow welding, while hot Immediately hammer or water quench to reduce the tendency of cracks. Surfacing metal austenitic high manganese steel, with work hardening, tough and wear-resistant characteristics. Mo is added to the weld metal to improve crack and wear resistance.
use:
Applicable to all kinds of crusher, high manganese rail, bucket, bulldozers and other parts subject to impact and easy surfacing.
Deposited metal chemical composition (%)
| C | Mn | Si | Mo | Other elements of the total |
guarantee value | ≤1.10 | 11.00 ~ 18.00 | ≤1.30 | ≤2.50 | ≤1.00 |
Example value | 0.65 | 14.60 | 0.75 | 1.00 |
|
Surfacing layer hardness:
HB ≧ 170
Reference current (AC, DC + )
Electrode diameter (mm) | φ3.2 | φ4.0 | φ5.0 |
Welding current (A) | 70 ~ 90 | 100 ~ 140 | 150 ~ 180 |
Precautions:
1. Before welding electrodes to be 300 ~ 350 ℃ baking 1h.
2. Surfacing has worn high manganese steel parts, prior to the fatigue layer should be eradicated or tough water treatment or chromium-manganese steel electrode (such as D277) primer.
3. When surfacing a lot of yellow smoke, should pay attention to strengthening ventilation and stand in the upper position for operation.