MH0Cr19Ni12Mo2
Description:
The main wire is 18Cr-12Ni-2Mo. Equipped with pressure-bearing stainless steel smelting equipment JQ.SJ601, the deposited metal has good mechanical properties, crack resistance, anti-intergranular corrosion resistance. Due to high alloy content, excellent corrosion resistance.
use:
Often used in pressure equipment, petrochemical, fertilizer equipment, such as 06Cr17Ni12Mo2 (SUS 316) and other materials welding.
Wire chemical composition (%)
| C | Mn | Si | Cr | Ni | Mo | P | S |
guarantee value | ≤0.080 | 1.00 ~ 2.50 | ≤0.60 | 18.00 ~ 20.00 | 11.00 ~ 14.00 | 2.00 ~ 3.00 | ≤0.030 | ≤ 0.010 |
Example value | 0.035 | 1.77 | 0.58 | 18.96 | 11.87 | 2.21 | 0.017 | 0.008 |
Deposited metal chemical composition (with pressure JQ.SJ601) (%)
| C | Mn | Si | Cr | Ni | Mo | P | S |
guarantee value | ≤0.08 | 0.50 ~ 2.50 | ≤1.00 | 17.0 ~ 20.0 | 11.0 ~ 14.0 | 2.00 ~ 3.00 | ≤0.030 | ≤0.020 |
Example value | 0.04 | 1.68 | 0.57 | 19.37 | 12.50 | 2.54 | 0.019 | 0.007 |
Deposited metal mechanical properties (with pressure JQ.SJ601)
experimental project | Rm (N / mm 2 ) | A (%) | With flux |
guarantee value | ≥520 | ≥25 | JQ.SJ601 |
Example value | 593 | 37 | JQ.SJ601 |
Reference current (AC, DC + )
Diameter (mm) | φ2.5 | φ3.2 | φ4.0 | φ5.0 |
Welding current (A) | 400 ~ 500 | 450 ~ 550 | 500 ~ 600 | 550 ~ 650 |
Precautions:
1. Welding temperature between the proposed control at about 150 ℃. Small and medium size multi-channel multi-layer welding, pay attention to control the welding line energy.
2. Welding parts of the rust layer, moisture, oil, dust, etc. really want to clean up.
3 flux before use to be 300 ~ 350 ℃ baking 2h.
The above suggestions are for reference only, in the specific operation to the scene prevail. If necessary, process assessment and then determine the welding program.