H08MnA
Description:
Manganese low silicon type wire, and manganese, silicon flux match, the base metal is not sensitive to rust, weld bead forming and slag performance. Single, bipolar, AC, DC welding can be.
use:
101 with sintered flux, 420N / mm 2 high-speed welding and filled with weld tensile strength of the base metal levels can be.
Wire chemical composition (%)
| C | Mn | Si | S | P | Cr | Ni | Cu |
guarantee value | ≤0.10 | 0.80 ~ 1.10 | ≤0.07 | ≤0.030 | ≤0.030 | ≤0.20 | ≤0.30 | ≤0.35 |
Example value | 0.066 | 0.96 | 0.038 | 0.007 | 0.010 | 0.027 | 0.011 | 0.110 |
Deposited metal mechanical properties
| Rm (N / mm 2 ) | ReL / Rp 0.2 (N / mm 2 ) | A (%) | KV 2 (J) -20 ° C |
|
SJ101 | 415 ~ 550 | ≥330 | ≥22 | ≥27 |
Wire specifications
Wire diameter (mm) | φ2.5 | φ3.2 | φ4.0 | φ5.0 |