H10MnSi
Description:
Manganese, moderate silicon content, and low manganese, silicon flux match, the base metal is not sensitive to rust, weld bead forming and slag performance. High welding efficiency.
use:
101 with sintered flux, 420N / mm 2 high-speed welding and filled with weld tensile strength of the base metal levels can be. Used for welding of boilers, pressure vessels, bridges, ships and other projects.
Wire chemical composition (%)
project | C | Mn | Si | S | P | Cr | Ni | Cu |
guarantee value | ≤0.14 | 0.80 ~ 1.10 | 0.60 ~ 0.90 | ≤0.035 | ≤0.035 | ≤0.20 | ≤0.30 | ≤0.35 |
Example value | 0.089 | 0.98 | 0.67 | 0.023 | 0.032 | 0.015 | 0.034 | 0.11 |
Deposited metal mechanical properties
| Rm (N / mm 2 ) | ReL / Rp 0.2 (N / mm 2 ) | A (%) | KV 2 (J) |
-20 ° C |
SJ101 | 415 ~ 550 | ≥330 | ≥22 | ≥27 |
Wire specifications
Wire diameter (mm) | φ2.5 | φ3.2 | φ4.0 | φ5.0 |