MH00Cr19Ni12Mo2
Description:
The main component of the wire is ultra-low C-18Cr-12Ni-2Mo. Equipped with JQ.SJ601 stainless steel alkaline sintered flux, the deposited metal has good mechanical properties, crack resistance, resistance to intergranular corrosion. Due to high alloy content, C content is low, corrosion resistance is more excellent.
use:
Often used in petrochemical, fertilizer equipment, the important structure, such as 022Cr17Ni12Mo2 (SUS 316L) and other materials welding.
Wire chemical composition (%)
| C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
guarantee value | ≤0.030 | 1.00 ~ 2.50 | ≤0.60 | 18.00 ~ 20.00 | 11.00 ~ 14.00 | 2.00 ~ 3.00 | ≤0.030 | ≤0.020 | ≤0.75 |
Example value | 0.024 | 1.75 | 0.48 | 18.68 | 11.66 | 2.20 | 0.024 | 0.014 | - |
Deposited metal (with flux: JQ.SJ601) Chemical composition (%)
| C | Mn | Si | Cr | Ni | Mo | P | S |
guarantee value | ≤0.040 | 0.50 ~ 2.50 | ≤1.00 | 17.00 ~ 20.00 | 11.0 ~ 14.0 | 2.00 ~ 3.00 | ≤0.040 | ≤0.030 |
Example value | 0.031 | 1.69 | 0.48 | 19.00 | 11.31 | 2.43 | 0.013 | 0.010 |
Deposited metal mechanical properties
experimental project | Rm (N / mm 2 ) | A (%) | With flux |
guarantee value | ≥480 | ≥30 | JQ.SJ601 |
Example value | 578 | 38 | JQ.SJ601 |
Reference current (AC, DC + )
Diameter (mm) | φ2.5 | φ3.2 | φ4.0 | φ5.0 |
Welding current (A) | 400 ~ 500 | 450 ~ 550 | 500 ~ 600 | 550 ~ 650 |
Precautions:
1. Welding temperature between the proposed control at about 150 ℃. Small and medium size multi-channel multi-layer welding, pay attention to control the welding line energy.
2. Welding parts of the rust layer, moisture, oil, dust, etc. really want to clean up.
3 flux before use to be 300 ~ 350 ℃ baking 2h.
The above suggestions are for reference only, in the specific operation to the scene prevail. If necessary, process assessment and then determine the welding program.