J857T
Description:
J606RH N pressure vessel 590 is / mm 2 ultra low potassium type high toughness steel welding crack-free use, AC and DC. Has a good notch impact toughness and crack resistance, can be all-position welding.
use:
For welding pressure vessels, bridges, hydropower down pipe and marine engineering and other important structures, and CF60 (62) steel to achieve a good match.
Deposited metal chemical composition (%)
| C | Mn | Si | S | P | Ni | Mo |
guarantee value | ≤0.10 | ≥1.00 | ≤0.80 | ≤0.025 | ≤0.025 | 0.60 ~ 1.20 | 0.10 ~ 0.40 |
Example value | 0.087 | 1.31 | 0.23 | 0.006 | 0.017 | 1.14 | 0.18 |
Deposited metal mechanical properties (620 ℃ × 1h)
Pilot projects | Rm (N / mm 2 ) | ReL / Rp 0.2 (N / mm 2 ) | A (%) | KV 2 (J) |
-40 ℃ |
guarantee value | ≥590 | ≥490 | ≥17 | ≥47 |
Example value | 685 | 610 | twenty one | 76 |
Deposited metal diffusion hydrogen content: ≤ 4.0ml / 100g (chromatography or mercury method)
X-ray detection: I level
Reference current (AC, DC + )
Electrode diameter (mm) | φ3.2 | φ4.0 | φ5.0 |
Welding current (A) | 80 ~ 120 | 130 ~ 180 | 170 ~ 240 |
Precautions:
1. Before welding electrode to be about 350 ~ 400 ℃ baking 1h, on the 100 ~ 150 ℃ incubator, with the use of take.
2. Welder should be removed before welding rust, oil, water and other impurities.