H10MnSiA
Description:
Manganese, moderate silicon content, and low manganese, silicon flux match, the base metal is not sensitive to rust, weld bead forming and slag performance. High welding efficiency.
use:
101 with sintered flux, 420N / mm 2 high-speed welding and filled with weld tensile strength of the base metal levels can be. Used for welding of boilers, pressure vessels, bridges, ships and other projects.
Deposited metal chemical composition (%)
| C | Mn | Si | S | P | Cr | Ni | Cu |
guarantee value | 0.06 ~ 0.15 | 0.90 ~ 1.40 | 0.45 ~ 0.75 | ≤0.030 | ≤0.025 | ≤0.20 | ≤0.30 | ≤0.35 |
Example value | 0.089 | 1.11 | 0.68 | 0.023 | 0.020 | 0.015 | 0.033 | 0.11 |
Deposited metal mechanical properties
| Rm (N / mm 2 ) | ReL / Rp 0.2 (N / mm 2 ) | A (%) | KV 2 (J) |
0 ° C | -20 ° C |
SJ101 | 415 ~ 550 | ≥330 | ≥22 | - | ≥27 |
Wire specifications
Wire diameter (mm) | φ2.5 | φ3.2 | φ4.0 | φ5.0 |