YD397
YD397 is a flux-cored flux-cored welding wire used for welding. The shielding gas can be mixed with CO 2 or 80% Ar + 20% CO 2. The welding process is good, the arc is stable, the splash is small, the slag is easy to break off and the crack is not cracked. Has a good high temperature hardness, stable performance. Preheat the specimen should be preheated to about 400 ℃, after welding about 550 ℃ tempering.
use:
Mainly used for hot forging die surfacing, die base metal 5CrNiMo, 5CrMnMo, the mold at high temperatures with good hardness and thermal fatigue resistance.
Deposited metal chemical composition (%) (shielding gas: 80% Ar + 20% CO 2 )
| C | Mn | Si | Cr | Mo | Ni |
guarantee value | ≤0.30 | ≤3.00 | ≤0.80 | 1.00 ~ 3.00 | ≤2.00 | ≤5.00 |
Surfacing metal hardness: (shielding gas: 80% Ar + 20% CO 2 )
Pilot projects | HRC |
General value | 36 ~ 42 |
Reference current (DC + )
Wire diameter (mm) | Current range (A) |
φ1.4 | 180 ~ 240 |
Precautions:
1 welding workpiece should be degreasing, rust treatment.
2. Welding, the gas flow is generally 20 ~ 25L / min.
3 flux cored welding, dry elongation should be 15 ~ 25mm.
4. Wire warehouse humidity should be maintained at less than 60%.
5. Non-vacuum packaging wire storage time should not exceed six months, vacuum packaging wire storage time should not exceed one year.